post heating meaning in Chinese

后期加热
后热(焊接)
回热

After dealing with post heating at the same deposit temperature , the average of transmission and reflectance of the films are smaller than unannealed ones but eopt is enlarged
相同沉积温度下制备的薄膜样品经过不同退火温度和退火时间处理后，薄膜的平均透过率和平均反射率都比退火前下降，光学能隙变大。
The photoluminescence of the thin films without post heating shows that the increasing of the deposit temperature decreases the pl intensity . only the sample deposited at 450 has one evident luminescence band found nearby 523 . 2nm
对复合镶嵌薄膜光致发光特性的研究发现，在450沉积未经过退火处理的薄膜样品中观察到室温光致发光现象，在523 . 2nm附近有一强的发光谱带。
The photoluminescence of the thin films without post heating is weak . only one luminescence band is found nearby 473nm . two luminescence bands are found after post heating , nearby 493nm and 368nm respectively . the intensity of the luminescence bands increase little by little when the temperature and the time of post heating continues to increase
而退火处理过后，薄膜出现两种光致发光现象，即蓝色发光和紫外发光，其峰值分别在493nm和368nm附近，而且随着退火温度的升高和退火时间的延长，发光谱带的强度逐渐增大，峰形的位置也有不明显的蓝移。